AMS 5513 2B Stainless Steel Precision Strip Roll 4mm Thickness

304 Stainless Strip, Coil, Foil & Wire, AMS 5513, AMS 5910 (1/4H), AMS 5911 (1/2H), AMS 5912 (3/4H), AMS 5913 (FH), AMS 5501 (1/4H), ASTM A666

AMS 5513 304 Stainless steel strips coil Annealed No.1 2B Annealed For general industry overview

Stainless steel 304 is an austenitic grade of stainless steel that contains high nickel content, typically somewhere between 8 and 10.5 percent by weight and a high amount of chromium that comprises approximately 18 to 20 percent by weight. The lower carbon content of grade 304 stainless steel minimizes chromium carbide precipitation from welding and the alloy’s susceptibility to intergranular corrosion.

304 stainless strip can achieve high hardness and strength through cold working. In the annealed condition, type 304 stainless steel strip is very ductile and can be cold worked easily through operations like roll forming, deep drawing, bending, and other common manufacturing processes. Stainless steel 304 strip is often specified for these characteristics given its high ductility, excellent drawing, forming, and spinning properties. The alloy work hardens rapidly, but in-process annealing is sometimes necessary to restore desirable ductility characteristics and lower hardness.

The 304 grade of stainless steel is known to have better corrosion resistance than Type 302. In regards to magnetic properties, 304 stainless steel is essentially non-magnetic, and only becomes slightly magnetic when cold worked. It has resistance to moderately aggressive organic acids is a result of the 9 to 11% nickel that the 304 alloys contain. Type 304 stainless steel strip also has resistance to corrosion in oxidizing environments is a result of the 18 to 19% chromium that the 304 alloys contain.

The alloy also exhibits excellent toughness, even down to cryogenic temperatures. On the other side of the spectrum, in terms of resistance to oxidation, this stainless steel alloy can be exposed to temperatures of about 1650F continuously appreciable scaling.

Type 304 can be easily welded using common fusion and resistance methods, like most other austenitic grades.

PRODUCT FORMS:

Sheet, plate , Strip, pipe ,tube ,bar ,profiles

Equivalent Materials

AMS 5513 304 Stainless steel strips coil Annealed No.1 2B Annealed For general industry Products Specification and Dimension Ranges

Hot Rolled Strip Available Size

Width: 16.0~609.6 mm
Thickness: 2.5~10.0 mm
Available Steel Grade:

Cold Rolled Strip Available Size

Width: 4.0~609.6 mm
Thickness: 0.1~3.0 mm

Surface Finish:

2B, 2D, BA, No.3, No.4, No.5, SB, HL, etc

Condition :

ANNEALED CONDITION

Ultimate Tensile Strength: 95 KSI min (655 MPA min) Yield Strength (0.2% Offset): 38 KSI min (260 MPA min) Elongation: 40%min Hardness: B95 max

TEMPERED 1/16 HARD

Ultimate Tensile Strength: 95 KSI min (655 MPA min) Yield Strength (0.2% Offset): 45 KSI min (310 MPA min) Elongation: 40% min

Tempered 1/8 Hard Ultimate Tensile Strength: 100 KSI min (690 MPA min) Yield Strength (0.2% Offset): 55 KSI min (380 MPA min) Elongation: 45% min

TEMPERED 1/4 HARD

Ultimate Tensile Strength: 125 KSI min (860 MPA min) Yield Strength (0.2% Offset): 75 KSI min (515 MPA min) Elongation: 25% min

TEMPERED 1/2 HARD

Ultimate Tensile Strength: 150 KSI min (1035 MPA min) Yield Strength (0.2% Offset): 110 KSI min (760 MPA min) Elongation: 15% < 0.15" 18% > 0.15"

TEMPERED 3/4 HARD

Ultimate Tensile Strength: 175 KSI min (1205 MPA min) Yield Strength (0.2% Offset): 135 KSI min (930 MPA min) Elongation: 10% < 0.15" 12% > 0.15"

TEMPERED FULL HARD

Ultimate Tensile Strength: 185 KSI min (1275 MPA min) Yield Strength (0.2% Offset): 140 KSI min (965 MPA min) Elongation: 8% < 0.15" 9% > 0.15"

Available Steel Grade:

Stainless steel : Type 201, 202, 205, 301, 302, 302B, 303, 303Se, 304, 304L, 302HQ, 304N, 305, 308, 309, 309S, 310, 310S, 314, 316, 316L, 316F, 316N, 317, 317L, 317LMN, 321, 330, 347, 348, 384, 405, 409, 429, 430, 430F, 430FSe, 434, 436, 442, 446, 403, 410, 414, 416, 416Se, 420, 420F, 422, 431, 440A, 440B, 440C, 630 , 13-8 PH ,15-5 PH , 17-7 PH ,17-4 ph , 904L , A286 ,VG-10 , SAE 316 , SAE 316L , SAE 440 , SAE 420

Duplex stainless steel : 2205 , 2304 , 2507

Nickel alloy :

Titanium and titanium alloys

AMS 5513 304 Stainless steel strips coil Annealed No.1 2B Annealed For general industry Application

AMS 5513 304 Stainless steel strips coil Annealed No.1 2B Annealed For general industry Technical datasheet

ADDITIONAL PROPERTIES

FINISHES

# 1 - Hot rolled annealed and descaled. It is available in strip, foil and ribbon. It is used for applications where a smooth decorative finish is not required.

# 2D - Dull finish produced by cold rolling, annealing and descaling. Used for deep drawn parts and those parts that need to retain lubricants in the forming process.

# 2B - Smooth finish produced by cold rolling, annealing and descaling. A light cold rolling pass is added after anneal with polished rolls giving it a brighter finish than 2D. #BA- Bright annealed cold rolled and bright annealed #CBA- Course bright annealed cold rolled matte finish and bright anneal

#2 - Cold Rolled

# 2BA- Smooth finish produced by cold rolling and bright annealing. A light pass using highly polished rolls produces a glossy finish.

2BA finish may be used for lightly formed applications where a glossy finish is desired in the formed part. Polished - Various grit finish for specific polish finished requirements. * Special finishes are available for all alloys - Contact US for more information.

AMS 5513 304 Stainless steel strips coil Annealed No.1 2B Annealed For general industry Products display and Package Details