Wuxi Zhongxin Special Steel Co.，Ltd
High Quality. High Performance. Competitive Price.
Add to Cart
thickness 0.2mm width 30mm Carburization Precision Stainless Steel Strip Carbon ASTM B536
Hot Rolled Strip Available Size
Width: 16.0~609.6 mm
Thickness: 2.5~10.0 mm
Available Steel Grade:
Cold Rolled Strip Available Size
Width: 4.0~609.6 mm
Thickness: 0.1~3.0 mm
Sheet, plate , Strip, pipe ,tube ,bar ,profiles
330 stainless steel Equivalent Materials
DIN 1.4864
EN 1.4864
EN X12NiCrSi365-16
DIN X12NiCrSi365-16
UNS N08330
AFNOR Z12NCS35.16
321 Stainless Steel Specifications:
ASTM A240 for annealed condition
ASTM A666 for tempered material
Surface Finish:
2B, 2D, BA, No.3, No.4, No.5, SB, HL, etc
| Surface finish | Characteristics and application |
| NO.2B | The surface brightness and flatness of no2B is better than no2D. then through a special surface treatment to improve its mechanical properties,No2B could nearly satisfy compreh ensive uses. |
| NO.1 | The surface is finished by heat treatment and pickling or processes corresponding thereto after hot rolling. |
| NO.4 | Polished with abrasive belt of grit #150-#180,have better brightness with discontinuous coarse stria,but thinner than No3, are used as bathtub buildings inner and external ornaments electrical appliances kitchen utensils and food processing equipment etc. |
| HL | Polished with abrasive belt of grit #150#320 on the NO.4 finish and has continuous streaks,mainly used as buildingsornaments elevators,door of building,frontal plate etc. |
| BA | Cold rolled, bright annealed and skin-passed, the product have excellent brightness and good reflexivity like mirror,kitchen apparatus,ornament etc. |
| 8K | The product have excellent brightness and prefer reflexivity can to be the mirror. |
Condition :
ANNEALED CONDITION
Ultimate Tensile Strength: 95 KSI min (655 MPA min) Yield Strength (0.2% Offset): 38 KSI min (260 MPA min) Elongation: 40%min Hardness: B95 max
TEMPERED 1/16 HARD
Ultimate Tensile Strength: 95 KSI min (655 MPA min) Yield Strength (0.2% Offset): 45 KSI min (310 MPA min) Elongation: 40% min
Tempered 1/8 Hard Ultimate Tensile Strength: 100 KSI min (690 MPA min) Yield Strength (0.2% Offset): 55 KSI min (380 MPA min) Elongation: 45% min
TEMPERED 1/4 HARD
Ultimate Tensile Strength: 125 KSI min (860 MPA min) Yield Strength (0.2% Offset): 75 KSI min (515 MPA min) Elongation: 25% min
TEMPERED 1/2 HARD
Ultimate Tensile Strength: 150 KSI min (1035 MPA min) Yield Strength (0.2% Offset): 110 KSI min (760 MPA min) Elongation: 15% < 0.15" 18% > 0.15"
TEMPERED 3/4 HARD
Ultimate Tensile Strength: 175 KSI min (1205 MPA min) Yield Strength (0.2% Offset): 135 KSI min (930 MPA min) Elongation: 10% < 0.15" 12% > 0.15"
TEMPERED FULL HARD
Ultimate Tensile Strength: 185 KSI min (1275 MPA min) Yield Strength (0.2% Offset): 140 KSI min (965 MPA min) Elongation: 8% < 0.15" 9% > 0.15"
Available Steel Grade:
Stainless steel : Type 201, 202, 205, 301, 302, 302B, 303, 303Se, 304, 304L, 302HQ, 304N, 305, 308, 309, 309S, 310, 310S, 314, 316, 316L, 316F, 316N, 317, 317L, 317LMN, 321, 330, 347, 348, 384, 405, 409, 429, 430, 430F, 430FSe, 434, 436, 442, 446, 403, 410, 414, 416, 416Se, 420, 420F, 422, 431, 440A, 440B, 440C, 630 , 13-8 PH ,15-5 PH , 17-7 PH ,17-4 ph , 904L , A286 ,VG-10 , SAE 316 , SAE 316L , SAE 440 , SAE 420
Duplex stainless steel : 2205 , 2304 , 2507
Nickel alloy :
Titanium and titanium alloys
Automotive and architectural trim, springs, kitchen and restaurant equipment and utensils, dairy and food processing equipment
CHEMISTRY TYPICAL
Carbon: 0.08 max
Manganese: 2.00 max
Silicon: 0.75 max
Chromium: 18.00-20.00
Nickel: 11.00-15.00
Molybdenum: 3.00-4.00
Phosphorus: 0.045 max
Sulfur: 0.030 max
Nitrogen: 0.10 max
PHYSICAL PROPERTIES
Density: 0.29 lbs/in3 7.99 g/cm3
Electrical Resistivity: microhm-in (microhm-cm):
68 ° F (20 ° C): 29.4 (74.0)
Specific Heat: BTU/lbl° F (kJ/kg•K): 32 - 212 ° F (0 - 100 °C): 0.12 (0.50)
Thermal Conductivity: BTU/hr/ft2/ft/°F (W/m•K):
At 212 °F (100 °C): 9.4 (16.2)
At 932 °F (500 °C): 12.4 (21.4)
Mean Coefficient of Thermal Expansion: in/inl°F (µm/m•K)
32 - 212 °F (0 - 100 °C): 8.9 x 10-5 (16.0)
32 - 600 °F (0 - 315 °C): 9.0 x 10-5 (16.2)
32 - 1000 °F (0 - 538 °C): 10.3 x 10-5 (18.5)
32 - 1500 °F (0 - 871 °C): 11.1 x 10-5 (18.5)
Modulus of Elasticity: ksi (MPa)
28 x 103 (193 x 103) in tension
11 .2 x 103 (77 x 103) in torsion
Magnetic Permeability: H = 200: Annealed < 1.02 max
Melting Range: 2500 - 2590 °F (1371 - 1421 °C)
FORMS
Coil - Sheet, Strip, Ribbon Wire - Profile, Round, Flat, Square
MECHANICAL PROPERTIES AT ROOM TEMPERATURE PROPERTIES: ANNEALED TYPICAL
Ultimate Tensile Strength: 75 KSI min (517 MPa min) Yield Strength: 30 KSI min (205 MPa min) Elongation: 35% min Hardness: Rb 95 max
PROPERTIES TEMPERED
Type 317 can be cold worked to various tempers. Contact US for additional information.
ADDITIONAL PROPERTIES
FINISHES
# 1 - Hot rolled annealed and descaled. It is available in strip, foil and ribbon. It is used for applications where a smooth decorative finish is not required.
# 2D - Dull finish produced by cold rolling, annealing and descaling. Used for deep drawn parts and those parts that need to retain lubricants in the forming process. # 2B - Smooth finish produced by cold rolling, annealing and descaling. A light cold rolling pass is added after anneal with polished rolls giving it a brighter finish than 2D.
#BA- Bright annealed cold rolled and bright annealed
#CBA- Course bright annealed cold rolled matte finish and bright anneal
#2 - Cold Rolled # 2BA- Smooth finish produced by cold rolling and bright annealing. A light pass using highly polished rolls produces a glossy finish. A 2BA finish may be used for lightly formed applications where a glossy finish is desired in the formed part. Polished - Various grit finish for specific polish finished requirements.
COLD FORMING
Type 317 can be readily formed and drawn.
HEAT TREATMENT
Type 317 is non hardenable by heat treatment.
Q: Would you provide samples For free?
A: Yes . with on stock specification We provide samples For Free . Freight charge collect
DIN 1.4864
EN 1.4864
EN X12NiCrSi365-16
DIN X12NiCrSi365-16
UNS N08330
AFNOR Z12NCS35.16