GH1035 is a Fe-Ni-Cr-based solid-solution-strengthening deformed superalloy, which is solid-solution-strengthened with elements such as chromium and tungsten. The operating temperature is below 900°C. The alloy has high thermal strength, the level is close to GH3039 nickel-based alloy. The alloy has good hot working plasticity and welding and cold forming process properties.
Chemical Composition Of The Ladle Analysis Of Gradegh1035
| C(％) | Si(％) | Mn(％) | P(％) | S(％) | Cr(％) | Ni(％) | W(%) | Nb(%) | Al(%) | Ti(%) | Other(%) |
|---|---|---|---|---|---|---|---|---|---|---|---|
| 0.06-0.12 | 0.8 | 0.7 | 0.03 | 0.02 | 20.0-23.0 | 35.0-40.0 | 2.50-3.50 | 1.20-1.70 | ≤0.50 | 0.70-1.20 | Ce≤0.05 |
Mechanical Properties Of Gradegh1035
| Proof strength Rp0.2(MPa) | Tensile strength Rm(MPa) | Impact energy KV(J) | Elongation at fracture A(%) | Reduction in cross section on fracture Z(%) | As-Heat-Treated Condition | Brinell hardness(HBW) |
|---|---|---|---|---|---|---|
| 829(≥) | 733(≥) | 11 | 32 | 42 | Solution and Aging,Annealing,Ausaging,Q+T,etc | 413 |
Gh1035 Range Of Products
| Product type | Products | Dimension | Processes | Deliver Status |
|---|---|---|---|---|
| Plates/Sheets | Plates/Sheets | 0.08-200mm(T)*W*L | Forging,hot rolling and cold rolling | Annealed,Solution and Aging,Q+T,ACID-WASHED,Shot Blasting |
| Steel Bar | Round Bar,Flat Bar,Square Bar | Φ8-1200mm*L | Forging,hot rolling and cold rolling,Cast | Black,Rough Turning,Shot Blasting, |
| Coil/Strip | Steel Coil/Steel Strip | 0.03-16.0x1200mm | Cold-Rolled&Hot-Rolled | Annealed,Solution and Aging,Q+T,ACID-WASHED,Shot Blasting |
| Pipes/Tubes | Seamless Pipes/Tubes,Welded Pipes/Tubes | OD:6-219mm x WT:0.5-20.0mm | Hot extrusion,Cold Drawn,Welded | Annealed,Solution and Aging,Q+T,ACID-WASHED |
Manufacture of flame tubes, combustor jackets, afterburners, guide rings and other annular parts of various aviation and aerospace engines.